AUTOCLAVED AERATED CONCRETE PANEL(AAC) ALC/AAC panel
AUTOCLAVED AERATED CONCRETE PANEL(AAC)Is the porous concrete, which composed of quartz sand, aluminum, lime, etc. as the main raw material, double-layer, two-way mesh reinforcement which is derusted and anticorrosion treatmented inside,Through high temperature, high pressure, steam curing etc.Is a new type of building materials with excellent performance at present.
1. Light weight: Bulk density 425~625kg/m³, Only for 1/4 concrete, 1/3 Clay brick, The weight of the building can be greatly reduced, and the design value is reduced too.
2. Fire resistance: 125mm AAC panel fire resistance can reach more than 4 hours, It is real fire prevention material in Grade A.50mm AAC panel can be met the fire protection requirements of steel structural members.
3. Anti crack: The shrinkage value of natural state is smaller than that of the clay brick, and the special technology is adopted to solve the problem of the quality of the slab cracks.
4. Thermal insulation: thermal insulation is only 0.11(B04), It is a new type of building material that can meet the building energy saving more than 65% by a single wall.
5. Seismic resistance: Allowable inter layer deflection angle 1/150, When the special node is used to achieve 1/120, In the case of all the nodes, the panel will not fall off when the 1/20 is changed in the layer;So that the anti-seismic effect is excellent.
6. Environmental protection: No radiation, Both the internal and external illumination coefficient are less than 0.1, is 1/4 of Fly ash board, Excellent sound insulation performance, 100mm AAC panel(Double sides putty)could reach 40.8dB, The sound insulation effect of is similar with 200mm fly ash brick wall.
7. Bearing capacity of Autoclaved Aerated Concrete Panel: The plates are equipped with internal double layers, two-way mesh reinforcement, can produce wall panels, partition wall, floor decking, roof board, decorative board etc..
8. economical: Using AAC board as the wall material, can effectively improve the use of the building area, reduce the use of energy consumption, to achieve the national building energy efficiency standards. Under the same sound insulation and fire protection requirements, AAC plate thickness is the smallest, and don't required the tie column, waist beam and other auxiliary components, This can reduce the wall load, thereby reducing the cost of construction.
9. Extensive: Can be used for concrete structure, steel structure residential buildings, office buildings, building internal and external wall body, floor slab, roof panel, firewall, explosion-proof wall, structural steel beams and columns fire maintenance, soundproof walls, old buildings and renovation.
10. Convenience: Eliminating the traditional building blocks in the process of the type of work, such as Mixing, masonry, plastering, reinforcement, formwork and concrete etc. Just the plate installation workers can do all the work, Avoid the conflict of work and mutual restraint.
Performance Indices in Grade B05 | |||||
Item | Unit | Detection value | Test standard | Standard | |
Dry bulk density | kg/m³ | 512 | GB/T11970-1997 | ±50 | |
Cube compressive strength (average) | Mpa | ≥4.0 | GB/T11971-1997 | ≥2.5 | |
Drying shrinkage | mm/m | 0.48 | GB/T11972-1997 | ≤0.8 | |
Coefficient of thermal conductivity (water content 5%) | W/m.k | 0.11 | GB/T10295-2008 | ≤0.14 | |
Frost | mass loss | % | 1 | GB/T11973-1997 | ≤5.0 |
Post freezing strength | Mpa | ≥2.0 | ≥2.0 | ||
Impact resistance (30kg sand pendulum impact back without crack) | times | ≥7.0 | JC666-1997 | 3 | |
The single point hanging force | N | 1200(100mm AAC) | JC666-1997 | ≥800 | |
1500(125mm AAC) | |||||
Bond strength between steel bar and AAC panel | Mpa | average value 2.4 | GB/T15762-2008 | ≥1.0 | |
Fire resistance limit of AAC plate | hour | 100mm wall: 3.62 | GB/T9978-2008 | ||
Protective steel column fire resistance limit in 50mm AAC panel | hour | >4.0 | GB/T9978-2008 | 4 | |
Protective steel beam fire resistance limit in 51mm AAC panel | hour | >3.0 | GB/T9978-2008 | 3 | |
Water softening coefficient R/R | % | 0.88 | GB/T11970-1997 | ||
Average | 100mm AAC panel+Both sides putty | dB | 41.8 | GBJ75-84 | |
125mm AAC panel+Both sides putty | 45.1 | ||||
150mm AAC panel+Both sides putty | 46.6 | ||||
175mm AAC panel+Both sides putty | 48.1 | ||||
200mm AAC panel+Both sides putty | 51.3 | ||||
Combination form-1(Both sides rock wool & AAC panel inside)150mm+40mm rock wool in both sides+10mm gypsum board(decoration)+Both sides putty | 55.2 | ||||
Combination form-2(Both sides AAC panel & rock wool inside)100mm AAC+50mm rock wool+100mm AAC | 58.6 | ||||
Dimension error | mm | L±3 | GB/T15762-2008 | L±4 | |
Surface smoothness | mm | 1 | GB/T15762-2008 | ≤3 | |
Linear expansion coefficient | /℃ | 7x10 | |||
Elastic modulus | N/mm | 1.75x10 | |||
Permeability (6 days 300mm high water spout drop height) | mm | 88.3 | refer to JISA5416-1997 | ≤100 |
Fire performance index of AAC inner wall plate | |||||
Wall thickness(mm) | 50 | 75 | 100 | 125 | 150 |
Fire resistance time(hour) | 1.57 | >2 | 3.62 | >4 | >4 |
Specification of AAC inner wall plate | ||||
Thickness(mm) | 75 | 100 | 125 | ≥150 |
Length(mm) | ≤3000 | ≤4000 | ≤5000 | ≤6000 |
Specification of AAC external wall plate | |||||
Thickness | 100 | 125 | 150 | 175 | 200 |
1.2KN/㎡ | 3600 | 4200 | 5200 | 6000 | 6000 |
1.4KN/㎡ | 3500 | 4200 | 4900 | 6000 | 6000 |
1.6KN/㎡ | 3300 | 4000 | 4700 | 5700 | 6000 |
1.8KN/㎡ | 3100 | 3900 | 4500 | 5400 | 6000 |
2.0KN/㎡ | 3000 | 3800 | 4300 | 5200 | 6000 |
2.2KN/㎡ | 2800 | 3600 | 4200 | 5000 | 5800 |
2.3KN/㎡ | 2700 | 3400 | 4100 | 4700 | 5600 |