Hot selling 30 mic metalized CPP film VMCPP for cosmetics packaging
Recyclable PET protective film is made of the CPP aluminium metalizing substrate film metalized in vacuum metalizing machine. It is usually divided into low temperature VMCPP, ultra-low temperature gas-filled VMCPP, high bonding strength VMCPP, low friction VMCPP corresponding to different functional applications. As heat sealing inner layer, VMCPP film is laminated with BOPP, BOPA, BOPET and other materials for bag making. It is suitable for various kinds of food, medicine and cosmetics packaging.
Protective Film Characteristic:
*Good barrier performance
*Excellent light-shading performance
*Excellent glossy appearance of aluminium metalizing layer,excellent foil ability to ink colour.
*Good laminating adaptability
*Excellent heat sealing strength
Physical and Mechanical Properties | ||||||||
Item Name | Standard Value | Typical Index | Testing Standard | |||||
Low temp | Ultra-low Temp & Inflatable | High BondingStrength | Low Friction | |||||
Tensile Strength Mpa | MD | ≥35 | 59 | 59 | 59 | 59 | ASTM D638 | |
TD | ≥25 | 38 | 38 | 38 | 38 | |||
Elongation at Break % | MD | ≥280 | 649 | 649 | 649 | 649 | ||
TD | ≥380 | 813 | 813 | 813 | 813 | |||
Thickness of Aluminum Layer Ω/ | ≤2.5 | 1.8 | 1.8 | 1.8 | 1.8 | ASTM D1003 | ||
Aluminum Layer Uniformity % | ±15% | ±8% | ±8% | ±8% | ±8% | |||
Bonding Strength of Aluminum Layer N (EAA Film Test upper seal knife 110℃, Lower seal knife 80℃) | Customized | 1.2-2.5 | ||||||
Heat Sealing Temperature ℃ (Non-treatment surface) | Heat Sealing Type | ≤145 | 122(≥8N) | 114(≥8N) | 122(≥8N) | 122(≥8N) | ||
Non-Sealing Type | >145 | |||||||
Surface Tension dyn/cm | Treatment Surface | ≥38 | ≥38 | ≥38 | ≥38 | ≥38 | ISO 8296 | |
Non-treatmentSurface | <33 | |||||||
Dynamic Friction Coefficient | Between Non-treatment Surfaces | 0.65-0.75 | 0.65-0.75 | 0.65-0.75 | 0.35-0.6 | ASTM D19 | ||
Previous: Our Child Resistant Pre-Roll Bags
Next: The Difference Between Soy Based Offset Ink And Ordinary Ink
Copyright：@2020-2021
Comments Please sign in or sign up to post.
0
0 of 500 characters used