Hot Dip Galvanized Low Carbon Steel Wire

Hot dipped galvanized wire is a kind of wire going through hot dipped galvanizing treatment.

Hot-dipped galvanizing is a physical reaction. After the chlorhydric acid pool and water pool, the iron wire will go through the drying panel and then enter the zinc stove. Hot-dip galvanizing is a form of galvanization. It is the process of coating iron, steel, or aluminum with a thin zinc layer, by passing the metal through a molten bath of zinc at a temperature of around 860 °F (460 °C). When exposed to the atmosphere, the pure zinc (Zn) reacts with oxygen (O2) to form zinc oxide (ZnO), which further reacts with carbon dioxide (CO2) to form zinc carbonate(ZnCO3), a usually dull grey, fairly strong material that stops further corrosion in many circumstances, protecting the steel below from the elements.

Customized products

2.54mm hot dipped galvanized wire (for making chain link mesh),the tolerance for wire diameter is ±0.02mm.The weight of per coil is 500kg and the coil inner diameter is 40 to 50 cm.
3.65mm hot dipped galvanized wire (Zinc thickness: min. 85.4g/M2,Wire tolerance ±0.02mm,500kg/coil)
wire,hot-dipped galvanized iron, 18 Ga ASTM A-641 for new spray shields

Material : Low carbon steel wire, medium carbon steel wire and high carbon steel wire.

Tensile Strength: 400--500MPA

Hot dipped iron wire Usage:  It mainly used in communication equipment, medical equipment and weaving nets, brushes, cables, filters, high pressure pipe, construction, handicrafts and other industries.

Standard wire gauge: 8# - 24#.(See the below table)

Specification: 

Hot Dipped Iron Wire in big packing

Production Process of Hot-dipped Galvanized Iron Wire:
Steel rod coil -- Wire Drawing -- Annealing -- Rust Removing -- Acid Washing -- Zinc Plating -- Wire Coil

Roping steel wire dia. 0.45 galv.1960 Mpa on MP300 / (hot dip galvanizing)
Tensile Strength – in the range 2400-2800 H/mm²
Coil wrap – about 250kg